- 產(chǎn)品名稱：奈米尼龍Ardlon-NE
- 簡介：
Ardlon-NE奈米尼龍，獨特性能如下：
高光澤高耐熱性，遠優(yōu)于一般塑料材料
優(yōu)良的電鍍表面質(zhì)量
成型加工良率高，降低成本
優(yōu)異的油氣阻隔性與耐沖擊性
詳細說明
兩個產(chǎn)品分別為：NE2640、NE8088。
NE2640是一種奈米級尼龍工程塑料，具有高表面平整性、耐熱性及耐沖擊性，并能在成形收縮率、塑料流動性及尺寸安定性等多方面取得適當(dāng)?shù)钠胶?，適用于仿烤漆表面或車燈無底涂之產(chǎn)品。
特性 | 測試方法 Test Method | 單位 | NE2640 | |
| 耐沖電鍍級 | ||||
| Plat. and Impact Grade | ||||
| DAM | 50%RH | |||
| 拉伸強度 | ASTM | Mpa | 80 | 70 |
| Tensile Strength | D-638 | |||
| 拉伸斷裂伸長率 | ASTM | % | 3.1 | 3.9 |
| Tensile Strain at Break | D-638 | |||
| 彎曲強度 | ASTM | Mpa | 140 | 132 |
| Flexural Strength | D-790 | |||
| 彎曲模數(shù) | ASTM | Mpa | 4125 | 3700 |
| Flexural Modulus | D-790 | |||
| 沖擊強度IZOD，切角 | ASTM | J/M | 71 | 131 |
| IZOD Impact Strength, Notched | D-256 | 23℃ | ||
| 熱變形溫度 | ASTM | ℃ | 125 | － |
| Heat Deflection Temperature at 1.82Mpa | D-648 | 192 | － | |
| Heat Deflection Temperature at 0.45Mpa | ||||
| 軟化點 | ASTM | ℃ | 212 | － |
| Vicat Softening Point(Rate B, Load 1) | D-1525 | |||
| 熔融指數(shù) (230℃，5kgs) | ASTM | g/10min | 22 | － |
| Melt Flow Index at 230℃, 5kgs | D-1238 | － | － | |
| Melt Flow Index at 230℃, 2.16kgs | ||||
| 比重 | ASTM | g/cm3 | 1.15 | |
| Specific Gravity | D-792 | |||
| 熔點 | ASTM | ℃ | 225 | |
| Melting Point | D-789 | |||
| 吸水率 (50%RH，24hrs) | ASTM | % | 0.1 | |
| Water Absorption, 50%RH | D-570 | |||
| 吸水率 (浸于水中，24hrs) | ASTM | % | 0.7 | |
| Water Absorption, In Water | D-570 | |||
| 成形收縮率（流動方向） | ASTM | % | 0.5~0.8 | |
| Mold Shrinkage (MD) | D-955 | |||
NE8088I 為一高阻氣性之奈米尼龍6復(fù)合材料。具有優(yōu)異的油氣外泄阻隔性及低溫耐沖擊強度，且具有高耐熱性。
特性 | 測試方法 Test Method | 單位 Unit | NE8088I | |
| 高阻氣、耐沖級 | ||||
| High barrier with super toughness | ||||
| DAM | 50%RH | |||
| 拉伸強度 | ASTM | Mpa | 50 | 47 |
| Tensile Strength | D-638 | |||
| 拉伸斷裂伸長率 | ASTM | % | 150 | 210 |
| Tensile Strain at Break | D-638 | |||
| 彎曲強度 | ASTM | Mpa | 62 | 54 |
| Flexural Strength | D-790 | |||
| 彎曲模數(shù) | ASTM | Mpa | 1600 | 1200 |
| Flexural Modulus | D-790 | |||
| 沖擊強度IZOD，切角 | ASTM | J/M | 900(23℃) | 1000 (23℃) |
| IZOD Impact Strength, Notched | D-256 | 23℃ | 750(-40℃) | 850 (-40℃) |
| 熱變形溫度 | ASTM | ℃ | 72 | － |
| Heat Deflection Temperature at 1.82Mpa | D-648 | 171 | － | |
| Heat Deflection Temperature at 0.45Mpa | ||||
| 熔融指數(shù) (230℃，5kgs) | ASTM | g/10min | 2.7 | |
| Melt Flow Index at 230℃, 5kgs | D-1238 | |||
| 比重 | ASTM | g/cm3 | 1.04 | |
| Specific Gravity | D-792 | |||
| 熔點 | ASTM | ℃ | 221 | |
| Melting Point | D-789 | |||
| 吸水率 (50%RH，24hrs) | ASTM | % | 0.18 | |
| Water Absorption, 50%RH | D-570 | |||
| 吸水率 (浸于水中，24hrs) | ASTM | % | 0.9 | |
| Water Absorption, In Water | D-570 | |||
| 成形收縮率（流動方向） | ASTM | % | 1.3~1.6 | |
| Mold Shrinkage (MD) | D-955 | |||